Gelled electrolyte for nanostructured lead-acid battery
2019
In recent years, the storage of energy produced by renewable sources has become a topic of great interest. Lead-acid batteries are widely used in this field, in particular those based on VRLA (Valve-Regulated-Lead Acid) technology, in which the electrolyte is immobilized inside the battery. In this paper, the use of a hydrogel as an electrolyte was considered. Hydrogel can be described as a three-dimensional network of a hydrophilic polymer that can absorb large amounts of water (or aqueous solutions) without dissolving. Pb and PbO2 nanostructured electrodes were used in the battery that used hydrogel as an electrolyte. Two different types of hydrogels were synthesised, both based on PVA th…
Nanostructured lead-acid negative electrode with reduced graphene oxide
2021
Aim of this work is to develop a new nano-structured and nano-composite lead acid negative electrode with reduced graphene oxide (rGO). Nanostructured electrodes are fabricated by template electrodeposition of lead nanowires on a lead current collector. A polycarbonate track-etched membrane was used as a template (200 nm mean pores diameter). rGO was deposited on the nanostructured electrode from a graphene oxide (GO) dispersion in acetate buffer solution (ABS) (0.2 g/L). Potentiostatic deposition of rGO at -0.8 V vs. standard calomel electrode (SCE) was performed. Electrode with rGO was tested as negative electrode in cell with 5M sulfuric acid solution, a commercial pasted positive plate,…
ULTRAFAST LEAD ACID BATTERIES USING NANOSTRUCTURED ELECTRODES
2012
Nanostructured Pb electrode for innovative lead-acid battery
2017
Lead-acid batteries are widely used for energy storage, due to a well-established and reliable technology. Over the years, various studies for improving the performance of this battery have been performed. The main goal is to replace conventional plates with innovative electrodes having good stability, high capacity and high surface area. In particular, it is necessary to improve the kinetics of electrochemical conversion reactions at the electrode-solution interface, and to guarantee good electrical continuity during repeated charge/discharge cycles. To achieve these goals, the attention was focused on nanostructured electrodes. Up-to-date, two principal approaches have been followed. In t…
LEAD-ACID BATTERIES WITH NANOSTRUCTURED ELECTRODES
2020
Lead Nanowires for Microaccumulators Obtained Through Indirect Electrochemical Template Deposition
2010
Metallic lead nanowires were deposited within pores of commercial anodic alumina membranes having an average pore diameter of 210 nm. "Direct" electrodeposition was attempted from 0.1 M Pb(NO 3 ) 2 aqueous solution with a variable concentration of H 3 BO 3 as a chelating agent, but it gave unsatisfactory results. An "indirect" two-step deposition procedure was then adopted, consisting of the anodic electrodeposition of α-PbO 2 nanowires, followed by their in situ reduction to metallic lead. Both these processes occurred at a high rate so that the indirect method led to a complete template pore filling with pure polycrystalline Pb in short times and with a high current efficiency.